品名： PA66 牌号：GF20 厂家：美国TPC
规格用途| 规格级别 | 增强 其它 其它 | 外观颜色 | nan |
| 该料用途 | 电动工具 电气外壳 纺织器材等 | ||
| 备注说明 | 优异的强度刚性和热变形温度 | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 机械性能 | 洛氏硬度 | R-Scale | ASTM D-785 | 117 | |
| 拉伸屈服强度 | ASTM D-638 | 117 | MPa | ||
| 拉伸断裂伸长率 | ASTM D-638 | 3.5 | % | ||
| 弯曲模量 | ASTM D-790 | 8270 | MPa | ||
| 弯曲强度 | ASTM D-790 | 190 | MPa | ||
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D-256 | 53.4 | J/m | |
| 洛氏硬度 | R-Scale | ASTM D-785 | 122 | ||
| 拉伸屈服强度 | ASTM D-638 | 107 | MPa | ||
| 拉伸断裂伸长率 | ASTM D-638 | 9 | % | ||
| 弯曲模量 | ASTM D-790 | 4830 | MPa | ||
| 弯曲屈服强度 | ASTM D-790 | 152 | MPa | ||
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D-256 | 160 | J/m | |
| 洛氏硬度 | R-Scale | ASTM D-785 | 98 | ||
| 拉伸屈服强度 | ASTM D-638 | 133 | MPa | ||
| 拉伸断裂伸长率 | ASTM D-638 | 2.9 | % | ||
| 弯曲模量 | ASTM D-790 | 5520 | MPa | ||
| 弯曲屈服强度 | ASTM D-790 | 186 | MPa | ||
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D-256 | 74.7 | J/m | |
| 机械性能 | 拉伸模量 | ASTM D638 | 5154 | MPa | |
| 屈服抗张强度 | ASTM D638 | 96.5 | MPa | ||
| 弯曲模量 | ASTM D790 | 5170 | MPa | ||
| 屈服弯曲强度 | ASTM D790 | 121 | MPa | ||
| 悬壁梁缺口冲击强度 | 23℃,3.18mm | ASTM D256 | 53 | J/m | |
| 电气性能 | 体积电阻率 | ASTM D-257 | 1.0E+16 | Ohm.cm | |
| 电气强度 | ASTM D-149 | 18 | Kv/mm | ||
| 表面电阻 | ASTM D-257 | 1.0E+2-1.0E+5 | ohms | ||
| 体积电阻率 | ASTM D-257 | 1.0E+2-1.0E+5 | ohm·cm | ||
| 体积电阻率 | ASTM D-257 | 3.0E+16 | ohm·cm | ||
| 介电强度 | ASTM D-149 | 19 | kV/mm | ||
| 体积电阻率 | ASTM D-257 | 2.0E+16 | ohm·cm | ||
| 介电强度 | ASTM D-149 | 30 | kV/mm | ||
| 体积电阻率 | ASTM D-257 | 1.0E+16 | ohm·cm | ||
| 介电强度 | ASTM D-149 | 18 | kV/mm | ||
| 物理性能 | 拉伸强度 | 5mm/min | ASTM D-638 | 140 | Mpa |
| 成型收缩率 | ASTM D-955 | 0.4-0.7 | % | ||
| 拉伸强度 | 5mm/min | ASTM D-638 | 130 | Mpa | |
| 成型收缩率 | ASTM D-955 | 0.4-0.6 | % | ||
| 比重 | nan | ASTM-D792 | 1.26 | g/cm3 | |
| 模具收缩率 | nan | ASTM-D955 | 0.2-0.4 | % | |
| 比重 | nan | ASTM D-792 | 1.19 | g/cm3 | |
| 模具收缩率 | Flow,3.00mm | ASTM D-955 | 0.20-0.40 | % | |
| 成型收缩率 | ASTM D-955 | 0.4-0.8 | % | ||
| 成型收缩率 | ASTM D-955 | 0.4-0.6 | % | ||
| 成型收缩率 | ASTM D-955 | 0.4-0.8 | % | ||
| 比重 | ASTM D-792 | 1.20 | g/cm3 | ||
| 模具收缩率 | Flow(3.18mm) | ASTM D-955 | 0.15 | % | |
| 吸水率 | 24hr | ASTM D-570 | 0.13 | % | |
| 比重 | ASTM D-792 | 1.21 | g/cm3 | ||
| 模具收缩率 | Flow(3.18mm) | ASTM D-955 | 0.050 | % | |
| 吸水率 | 24hr | ASTM D-570 | 0.13 | % | |
| 成型收缩率-Flow | 3.18mm | ASTM D-955 | 0.7 | % | |
| 比重 | ASTM D792 | 1.04 | g/cm3 | ||
| 成型收缩率 | ASTM D955 | 0.4 | % | ||
| 吸水率 | ASTM D570 | 0.01 | % | ||
| 成型收缩率-Flow | 3.18mm | ASTM D-955 | 0.35 | % | |
| 成型收缩率-Flow | 3.18mm | ASTM D-955 | 0.4 | % | |
| 成型收缩率-Flow | 3.18mm | ASTM D-955 | 0.2 | % | |
| 密度 | ASTM D-792 | 1.22 | g/cm3 | ||
| 熔融指数 | 200℃,5kg | ASTM D-1238 | 5 | g/10min | |
| 尺寸收缩率 | 150×100×3.2mm | ASTM D-955 | 0.3-0.5 | % | |
| 密度 | ISO 1183 | 1.47 | g/cm³ | ||
| 密度 | ISO 1183 | 1.06 | g/cm3 | ||
| 熔化体积流率 | ISO 1133 | 8 | cm3/10min | ||
| 密度 | ISO 1183 | 1.35 | g/cm3 | ||
| 溶化体积流率 | 300℃/1.2 kg | ISO 1133 | 9.00 | cm3/10min | |
| 吸水率 | 23℃, 24 hr | ISO 62 | 0.30 | % | |
| 吸水率 | 平衡，23℃，50%RH | ISO 62 | 0.10 | % | |
| 密度 | ISO 1183 | 1.35 | g/cm3 | ||
| 溶化体积流率 | 300℃/1.2 kg | ISO 1133 | 10.0 | cm3/10min | |
| 吸水率 | 23℃, 24 hr | ISO 62 | 0.30 | % | |
| 吸水率 | 平衡，23℃，50%RH | ISO 62 | 0.10 | % | |
| 密度 | ISO 1183 | 1.35 | g/cm3 | ||
| 溶化体积流率 | 300℃/1.2 kg | ISO 1133 | 7.50 | cm3/10min | |
| 吸水率 | 23℃, 24 hr | ISO 62 | 0.30 | % | |
| 吸水率 | 平衡，23℃，50%RH | ISO 62 | 0.12 | % | |
| 密度 | ISO 1183 | 1.60 | g/cm3 | ||
| 吸水率 | 23℃, 24 hr | ISO 62 | 0.50 | % | |
| 吸水率 | 平衡，23℃，50%RH | ISO 62 | 0.20 | % | |
| 密度 |