品名： LDPE 牌号：1100 厂家：德国雷曼福斯
规格用途| 规格级别 | 其它 其它 注塑 | 外观颜色 | nan |
| 该料用途 | 适合通用制品 | ||
| 备注说明 | 特性：流动性好 | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 机械性能 | 洛氏硬度 | R-Scale | ASTM D-785 | 120 | |
| 拉伸屈服强度 | ASTM D-638 | 35.2 | MPa | ||
| 拉伸断裂伸长率 | ASTM D-638 | 4 | % | ||
| 弯曲模量 | ASTM D-790 | 6890 | MPa | ||
| 弯曲强度 | ASTM D-790 | 48.3 | MPa | ||
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D-256 | 347 | J/m | |
| 物理性能 | 固体比重 | nan | ASTM D-792 | 1.36 | nan |
| 模具收缩率 | nan | ASTM D-955 | 5-7 | in/inE-3 | |
| 比重 | ASTM D792, ISO 1183 | 1.31 | g/cm³ | ||
| 收缩率 | 流动 1.60 mm | ASTM D955 | 0.12-0.18 | % | |
| 吸水率 | 24 hr | ASTM D570 | 0.06 | % | |
| 吸水率 | 23℃, 24 hr | ISO 62 | 0.06 | % | |
| 密度 | nan | ISO 1183 | 1140 | kg/m3 | |
| 成型收缩率 | nan | ISO 294-4 | 1.6 | % | |
| 吸水率 | nan | ISO 62 | 8.5 | % | |
| 比重 | nan | ASTM D-792 | 1.06 | g/cm3 | |
| 模具收缩率 | Flow | ASTM D-955 | 0.40-0.60 | % | |
| 成型收缩率-Flow | 3.18mm | ASTM D-955 | 0.2 | % | |
| 比重 | ASTM D-792 | 1.09 | g/cm3 | ||
| 收缩率 | 流动,3.20mm | ASTM D-955 | 0.50-0.60 | % | |
| 比重 | ASTM D792 | 1.20 | g/cm3 | ||
| 熔流率 | ASTM D1238 | 11 | g/10min | ||
| 流动收缩率 | ASTM D955 | 0.50-0.70 | % | ||
| 吸水率 | 24hr | ASTM D570 | 0.15 | % | |
| 吸水率 | 饱和 | ASTM D570 | 0.35 | % | |
| 比重 | ASTM D792 | 1.31 | g/cm3 | ||
| 流动收缩率 | 3.18mm | ASTM D955 | 1.8 | % | |
| 吸水率 | 24 hr | ASTM D570 | 0.080 | % | |
| 洛氏硬度 | M 计秤 | ASTM D785 | 76 | ||
| 洛氏硬度 | R 计秤 | ASTM D785 | 116 | ||
| 比重 | ASTM D792 | 1.20 | g/cm3 | ||
| 流动收缩率 | 3.18mm | ASTM D955 | 0.60 | % | |
| 吸水率 | 24 hr | ASTM D570 | 0.15 | % | |
| 吸水率 | 饱和 | ASTM D570 | 0.35 | % | |
| 洛氏硬度 | M 计秤 | ASTM D785 | 78 | ||
| 其他 | 成型收缩率 | ASTM D955 | 1.4-2.5 | % | |
| 比重 | ASTM D792 | 1.31 | |||
| 机械性能 | 屈服挠曲强度 | nan | ASTM D-790 | 24000 | Psi |
| IZOD缺口冲击强度 | nan | ASTM D-256 | 0.7 | ft-lb/in | |
| 断裂抗拉伸伸长 | nan | ASTM D-638 | 70.0 | % | |
| 屈服抗拉强度 | nan | ASTM D-638 | 15900 | Psi | |
| 挠曲模量 | nan | ASTM D-790 | 54000 | Psi | |
| 拉伸应力 | 屈服 | ISO 527-2 | 56 | MPa | |
| 拉伸应变 | 断裂 | ISO 527-2 | > 150 | % | |
| 弯曲模量 | ISO 178 | 2450 | MPa | ||
| 弯曲强度 | ISO 178 | 81 | MPa | ||
| 拉伸轻度 | ASTM D638 | 600 | Kg/cm2 | ||
| 弯曲弹性率 | ASTM D790 | 24000 | Kg/cm2 | ||
| 缺口冲击强度 | ASTM D256 | 4 | kg.cm/cm | ||
| 拉伸模量 | nan | ISO 527-2/1A | 3000 | MPa | |
| 屈服拉伸强度 | nan | ISO 527-2/1A | 84 | MPa | |
| 屈服伸长率 | nan | ISO 527-2/1A | 5 | % | |
| Izod缺口冲击强度 | nan | ISO 180/1A | 5.2 | KJ/m2 | |
| 洛氏硬度 | nan | ISO 2039-2 | 82 | M | |
| 洛氏硬度 | nan | ASTM D-785 | 115 | R scale | |
| 拉伸屈服强度 | nan | ASTM D-638 | 53.8 | MPa | |
| 弯曲模量 | nan | ASTM D-790 | 3100 | MPa | |
| IZOD缺口冲击强度 | 23℃，3.18mm | ASTM D-256 | 26.7 | J/m | |
| 耐环境应力开裂性 | 100% lgepal F50 | ASTM D-1693B | 15.0 | hr | |
| 硬度 | nan | ASTM D-2240 | 65 | Shore D | |
| 拉伸屈服强度 | nan | ASTM D-638 | 30.1 | MPa | |
| 拉伸断裂强度 | nan | ASTM D-638 | 20.7 | MPa | |
| 断裂伸长率 | nan | ASTM D-638 | 750 | % | |
| 弯曲模量 | nan | ASTM D-790 | 1730 | MPa | |
| Izod缺口冲击强度 | 0℃ | ASTM D-256 | 102 | J/m | |
| Izod缺口冲击强度 | 23℃ | ASTM D-256 | 123 | J/m | |
| 抗张强度 | ASTM D-638 | 44.0 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 25 | % | ||
| 弯曲模量 | ASTM D-790 | 2500 | MPa | ||
| 弯曲强度 | ASTM D-790 | 73.0 | MPa | ||
| 悬壁梁缺口冲击强度 | 23℃ | ASTM D-256 | 150 | J/m | |
| 摩擦系数 | 与钢-动态 | ASTM D-1894 | 0.40 | ||
| 摩擦系数 | 与钢-静态 | ASTM D-1894 | 0.27 | ||
| 拉伸模量 | ASTM D638 | 2410 | MPa | ||
| 断裂抗张强度 | ASTM D638 | 72.4 | MPa | ||
| 屈服伸长率 | ASTM D638 | 5.5 | % | ||
| 断裂伸长率 | ASTM D638 | 120 | % | ||
| 弯曲模量 | ASTM D790 | 2340 | MPa | ||
| 弯曲强度 | ASTM D790 |