规格用途
| 规格级别 |
其它 其它 嵌段共聚注塑 |
外观颜色 |
nan |
| 该料用途 |
负重部件,汽车部件 |
| 备注说明 |
ICP,注塑级,高抗冲 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
I:21.6kg |
ASTM D-11238 |
2.5 |
g/10min |
| 密度 |
nan |
ASTM D-1505 |
0.90 |
g/cm3 |
| 密度 |
|
ASTM D-1505 |
0.90 |
g/cm3 |
| 熔体流动速率 |
|
ASTM D-1238 |
2.50 |
g/10min |
| 熔体流动速率 |
nan |
nan |
2.5 |
g/10min |
| 密度 |
nan |
nan |
0.9 |
kg/cm3 |
| 熔体流动速率 |
|
ASTM D-1238 |
2.5 |
g/10min |
| 密度 |
|
ASTM D-1505 |
0.9 |
g/cm3 |
| 热性能 |
热变型温度 |
nan |
ASTM D-648 |
90 |
℃ |
| 热变形温度 |
0.46MPa |
ASTM D-648 |
93 |
℃ |
| 热变形温度 |
0.46MPa |
nan |
93 |
℃ |
| 热变形温度 |
4.6kg/cm2 1/4〃厚 |
ASTM D-648 |
90 |
℃ |
| 热变形温度 |
0.46MPa |
ASTM D-648 |
93 |
℃ |
| 热变形温度 |
|
ISO 75 |
85 |
℃ |
| 其他性能 |
黄色指数 |
|
ASTM D-6290 |
2 |
% |