品名： PMMA 牌号：V 厂家：意大利SO.F.TER.
规格用途| 规格级别 | 其它 其它 注塑 | 外观颜色 | nan |
| 该料用途 | nan | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 熔体流动速率 | 230°C.3.8kg | ASTM D-1238 | 2.5 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.3 | % | |
| 吸水率 | 24hr | ASTM D-570 | 0.20 | % | |
| 吸水率 | 24hr | ASTM D-570 | 0.20 | % | |
| 吸水率 | 24hr | ASTM D-570 | 0.30 | % | |
| 热性能 | 热传递率 | nan | JIS A1412 | 0.2 | W/(m·℃) |
| 比热 | nan | JIS K7123 | 1.5 | J/(g·℃) | |
| 载荷挠曲温度 | 1.80MPa | ISO 75-2 | 94 | ℃ | |
| 维卡软化温度 | 50N | ISO 306 | 100 | ℃ | |
| 螺旋流动 | 厚薄2mm，250℃ | 三菱丽阳法 | 230 | mm | |
| 螺旋流动 | 厚薄2mm，230℃ | 三菱丽阳法 | 150 | mm | |
| 热膨胀系数 | nan | JIS K7197 | 6×10-5 | 1/℃ | |
| 熔体流动性 | 230℃，37.3N | ISO 1133 | 2.2 | g/10min | |
| 维卡软化点 | 1kg | ASTM D-1525 | 107 | °C | |
| 载荷挠曲温度 | 18.56kg/cm2 | ASTM D-648 | 92 | °C | |
| 比热 | nan | nan | 0.35 | cal/g/°C | |
| 线膨胀系数 | nan | ASTM D-696 | 6×10-5 | cm/cm/°C | |
| 热传导系数 | nan | ASTM C-177 | 5×10-4 | cal/s/cm/°C | |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 93.9 | ℃ | |
| CLTE | Flow | ASTM D-696 | 0.000090 | cm/cm/℃ | |
| 导热系数 | nan | ASTM C-177 | 0.16 | W/m.K | |
| 阻燃性 | 1.59mm | UL 94 | HB | nan | |
| 阻燃性 | 3.20mm | UL 94 | HB | nan | |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 100 | ℃ | |
| CLTE | Flow | ASTM D-696 | 0.000090 | cm/cm/℃ | |
| 导热系数 | nan | ASTM C-177 | 0.16 | W/m.K | |
| 阻燃性 | 1.59mm | UL 94 | HB | nan | |
| 阻燃性 | 3.20mm | UL 94 | HB | nan | |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 82.2 | ℃ | |
| CLTE | Flow | ASTM D-696 | 0.000090 | cm/cm/℃ | |
| 导热系数 | nan | ASTM C-177 | 0.17 | W/m.K | |
| 阻燃性 | 1.59mm | UL 94 | HB | nan | |
| 阻燃性 | 3.20mm | UL 94 | HB | nan | |
| 热稳定性 | CEI 20-34/3-2 | > 1 | hr | ||
| 热变形温度 | 0.45 MPa, 未退火, 6.35 mm | ASTM D648 | 141 | ℃ | |
| 1.8 MPa, 未退火, 6.35 mm | ASTM D648 | 135 | ℃ | ||
| 线形膨胀系数 - 流动 | 6.35 mm | ASTM D696 | 0.000068 | cm/cm/℃ | |
| 比热 | ASTM C351 | 1260 | J/kg/℃ | ||
| 导热系数 | ASTM C177 | 0.19 | W/m/K | ||
| 机械性能 | 拉伸永久变形 | ASTM D412 | 10 | % | |
| 拉伸应力 | 100%应变 | ASTM D412 | 2.50 | MPa | |
| 抗张强度 | 断裂 | ASTM D412 | 6.00 | MPa | |
| 伸长率 | 断裂 | ASTM D412 | 450 | % | |
| 撕裂强度 | ASTM D624 | 24.0 | kN/m | ||
| 压缩永久变形 | 70°C, 22.0 hr | ASTM D395B | 35 | % |