规格用途
| 规格级别 |
其它 家电部件 挤出,注塑 |
外观颜色 |
nan |
| 该料用途 |
垫圈，家电部件，家用货品，片材，汽车领域的应用 |
| 备注说明 |
可回收材料，一般目的 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 机械性能 |
硬度 |
邵氏 A, 5 秒 |
ASTM D2240 |
35 |
|
| 抗张强度 |
屈服 |
ASTM D638 |
5.30 |
MPa |
| 拉伸永久变形 |
100% 应变 |
ASTM D412 |
1 |
% |
| 拉伸应力 |
100% 应变 |
ASTM D412 |
0.785 |
MPa |
| 伸长率 |
断裂 |
ASTM D412 |
600 |
% |
| 撕裂强度 |
|
ASTM D624 |
10.8 |
kN/m |
| 压缩永久变形 |
23℃, 168 hr |
ASTM D395 |
10 |
% |
| 压缩永久变形 |
120℃, 70.0 hr |
ASTM D395 |
37 |
% |
| 硬度 |
邵氏 A, 5 秒 |
ASTM D2240 |
45 |
|
| 抗张强度 |
屈服 |
ASTM D638 |
6.96 |
MPa |
| 拉伸永久变形 |
100% 应变 |
ASTM D412 |
5 |
% |
| 拉伸应力 |
100% 应变 |
ASTM D412 |
1.86 |
MPa |
| 伸长率 |
断裂 |
ASTM D412 |
570 |
% |
| 撕裂强度 |
|
ASTM D624 |
15.7 |
kN/m |
| 压缩永久变形 |
23℃, 168 hr |
ASTM D395 |
16 |
% |
| 压缩永久变形 |
120℃, 70.0 hr |
ASTM D395 |
37 |
% |
| 硬度 |
邵氏 A, 5 秒 |
ASTM D2240 |
55 |
|
| 抗张强度 |
屈服 |
ASTM D638 |
7.65 |
MPa |
| 拉伸永久变形 |
100% 应变 |
ASTM D412 |
7 |
% |
| 拉伸应力 |
100% 应变 |
ASTM D412 |
2.45 |
MPa |
| 伸长率 |
断裂 |
ASTM D412 |
560 |
% |
| 撕裂强度 |
|
ASTM D624 |
21.6 |
kN/m |
| 压缩永久变形 |
23℃, 168 hr |
ASTM D395 |
19 |
% |
| 压缩永久变形 |
120℃, 70.0 hr |
ASTM D395 |
40 |
% |
| 硬度 |
邵氏 A, 5 秒 |
ASTM D2240 |
65 |
|
| 抗张强度 |
屈服 |
ASTM D638 |
9.12 |
MPa |
| 拉伸永久变形 |
100% 应变 |
ASTM D412 |
8 |
% |
| 拉伸应力 |
100% 应变 |
ASTM D412 |
2.94 |
MPa |
| 伸长率 |
断裂 |
ASTM D412 |
500 |
% |
| 撕裂强度 |
|
ASTM D624 |
29.4 |
kN/m |
| 压缩永久变形 |
23℃, 168 hr |
ASTM D395 |
22 |
% |
| 压缩永久变形 |
120℃, 70.0 hr |
ASTM D395 |
42 |
% |
| 硬度 |
邵氏 A, 5 秒 |
ASTM D2240 |
80 |
|
| 抗张强度 |
屈服 |
ASTM D638 |
9.32 |
MPa |
| 拉伸永久变形 |
100% 应变 |
ASTM D412 |
14 |
% |
| 拉伸应力 |
100% 应变 |
ASTM D412 |
4.31 |
MPa |
| 伸长率 |
断裂 |
ASTM D412 |
580 |
% |
| 撕裂强度 |
|
ASTM D624 |
47.1 |
kN/m |
| 压缩永久变形 |
23℃, 168 hr |
ASTM D395 |
32 |
% |
| 压缩永久变形 |
120℃, 70.0 hr |
ASTM D395 |
67 |
% |
| 热性能 |
脆化温度 |
|
ASTM D746 |
-60.0 |
℃ |
| 脆化温度 |
|
ASTM D746 |
-60.0 |
℃ |
| 脆化温度 |
|
ASTM D746 |
-60.0 |
℃ |
| 脆化温度 |
|
ASTM D746 |
-60.0 |
℃ |
| 脆化温度 |
|
ASTM D746 |
-60.0 |
℃ |
| 物理性能 |
比重 |
|
ASTM D792 |
0.928 |
g/cm³ |
| 比重 |
|
ASTM D792 |
0.948 |
g/cm³ |
| 比重 |
|
ASTM D792 |
0.948 |
g/cm³ |
| 比重 |
|
ASTM D792 |
0.958 |
g/cm³ |
| 比重 |
|
ASTM D792 |
1.19 |
g/cm³ |