规格用途
| 规格级别 |
其它 其它 均聚注塑 |
外观颜色 |
nan |
| 该料用途 |
机械零件汽车部件 |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
nan |
ASTM D-1505 |
0.91 |
g/cm3 |
| 熔体流动速率 |
nan |
ASTM D-1238 |
1.5 |
g/10min |
| 熔体流动速率 |
nan |
nan |
7.5 |
nan |
| 相对密度 |
nan |
nan |
0.918 |
nan |
| 熔体流动速率 |
200℃,5Kg |
ASTM D-1238 |
4.5 |
g/10min |
| 热性能 |
负载下热变形温度 |
66磅/英寸2 |
ASTM D-648 |
110 |
℃ |
| 维卡软化点 |
nan |
ASTM D-1525 |
160 |
℃ |
| 热变形温度 |
1.82MPa，经退火 |
ASTM D-648 |
99 |
℃ |
| 热变形温度 |
1.82MPa，未经退火 |
nan |
75 |
℃ |
| 线性热膨胀系数 |
10-5 |
nan |
7.6 |
cm/cm℃ |
| 维卡软化点 |
nan |
ASTM D-1525 |
105 |
℃ |
| 热变形温度 |
|
ASTM D648 |
65 |
℃ |
| 阻燃等级 |
|
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火,4.00mm |
ASTM D-648 |
198 |
℃ |
| UL阻燃等级 |
1.60mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火,4.00mm |
ASTM D-648 |
255 |
℃ |
| UL阻燃等级 |
1.60mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8 MPa, 退火, 注塑 |
ASTM D-648 |
93.0 |
℃ |
| 维卡软化温度 |
|
ASTM D-1525 |
106 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000080 |
cm/cm/℃ |
| UL阻燃等级 |
|
UL 94 |
HB |
|
| UL档案号 |
|
|
E57787 |
|
| 热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
120 |
℃ |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D648 |
60.0 |
℃ |
| 熔融温度 |
|
|
218～224 |
℃ |
| 流动线形膨胀系数 |
|
ASTM D696 |
0.000013 |
cm/cm/℃ |
| UL 阻燃等级 |
0.794mm |
UL 94 |
HB |
|
| UL 阻燃等级 |
1.59mm |
UL 94 |
HB |
|
| UL 阻燃等级 |
3.18mm |
UL 94 |
HB |
|
| UL 阻燃等级 |
6.35mm |
UL 94 |
HB |
|
| 热变形温度 |
1.82Mpa |
ASTM D648 |
55 |
℃ |
| 线膨胀系数 |
-30+30℃ |
ASTM D696 |
8.0x10-5 |
1/℃ |
| 燃烧性 |
3.2mm厚 |
UL 94 |
V-0 |
|