规格用途
| 规格级别 |
其它 纤维 其它 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
单丝 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.91 |
g/cm3 |
| 熔体流动速率 |
|
ASTM D-1238 |
2.5 |
g/10min |
| 相对密度 |
nan |
nan |
0.923 |
nan |
| 熔体流动速率 |
nan |
nan |
4.4 |
nan |
| 密度 |
nan |
ASTM D-1905 |
0.954 |
g/cm3 |
| 熔体流动速率 |
nan |
ASTM D-1238 |
0.80 |
g/10min |
| 比重 |
|
ASTM D792 |
1.37 |
g/cm3 |
| 熔流率 |
380℃/2.16kg |
ASTM D1238 |
42 |
g/10min |
| 流动收缩率 |
|
ASTM D955 |
0.60 |
% |
| 吸水率 |
24hr |
ASTM D570 |
0.50 |
% |
| 吸水率 |
30 days |
ASTM D570 |
1.9 |
% |
| 热性能 |
热变形温度 |
66磅/英寸² |
ASTM D-648 |
110 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
160 |
℃ |
| 维卡软化点 |
nan |
ASTM D-1525 |
123 |
℃ |
| 脆化温度 |
nan |
ASTM D-746 |
<-80 |
℃ |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D648 |
200 |
℃ |
| 流动线形膨胀系数 |
|
ASTM D696 |
0.000052 |
cm/cm/℃ |
| UL 阻燃等级 |
1.50mm |
UL 94 |
V-0 |
|
| 热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
87.8 |
℃ |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D648 |
82.2 |
℃ |
| 流动线形膨胀系数 |
|
ASTM D696 |
0.000072 |
cm/cm/℃ |