规格用途
规格级别 |
其它 其它 挤出 |
外观颜色 |
nan |
该料用途 |
nan |
备注说明 |
nan |
技术参数
项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
基本性能 |
密度 |
nan |
ISO 1183 |
1.03 |
g/cm3 |
熔体流动速率 |
220℃,10kg |
ISO 1133 |
10 |
g/10min |
吸水率 |
23℃,24hr |
ISO 62 |
0.30 |
% |
密度 |
nan |
ASTM D-1505 |
0.939 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.33 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
3.5 |
g/10 min |
密度 |
nan |
ASTM D-1505 |
0.939 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.30 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
3.5 |
g/10min |
密度 |
nan |
ASTM D-1505 |
0.939 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.35 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
5.0 |
g/10 min |
密度 |
nan |
g/cm3 |
0.939 |
ASTM D-1505 |
表观密度 |
nan |
ASTM D-1895 |
0.35 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
5.0 |
g/10min |
密度 |
nan |
ASTM D-1505 |
0.934 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.35 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
5.0 |
g/10min |
密度 |
nan |
ASTM D-1505 |
0.934 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.35 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
5.0 |
g/10min |
密度 |
nan |
ASTM D-1505 |
0.939 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.35 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
3.0 |
g/10min |
密度 |
nan |
ASTM D-1505 |
0.939 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.35 |
g/cm3 |
熔体流动速率 |
100% lgepal CO-630,F50 |
ASTM D-1238 |
3.0 |
g/10min |
密度 |
nan |
ASTM D-1505 |
0.939 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.35 |
g/cm3 |
熔体流动速率 |
nan |
ASTM D-1238 |
3.0 |
g/10min |
密度 |
nan |
ASTM D-1505 |
0.939 |
g/cm3 |
表观密度 |
nan |
ASTM D-1895 |
0.33 |
g/cm3 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
3 |
g/10min |
热性能 |
维卡软化温度 |
nan |
ISO 306 |
97.0 |
℃ |
线膨胀系数 |
23℃-55℃ |
ISO 11359-1,-2 |
0.000090 |
cm/cm℃ |
燃烧性 |
nan |
1.50mm |
HB |
UL 94 |
维卡软化温度 |
nan |
ASTM D-1525 |
121 |
℃ |
维卡软化温度 |
nan |
ASTM D-1525 |
120 |
℃ |
维卡软化温度 |
nan |
ASTM D-1525 |
119 |
℃ |
维卡软化温度 |
nan |
ASTM D-1525 |
118 |
℃ |
熔化温度 |
nan |
DSC |
125 |
℃ |
熔化温度 |
nan |
DSC |
125 |
℃ |
熔化温度 |
nan |
DSC |
125 |
℃ |
熔化温度 |
nan |
DSC |
125 |
℃ |
热变形温度 |
1.8 MPa, 未退火 |
ISO 75-2/Ae |
143 |
℃ |
维卡软化点 |
|
ISO 306/A |
119 |
℃ |
阻燃等级 |
1.60 mm |
UL 94 |
HB |
|
热变形温度 |
1.8 MPa, 未退火 |
ISO 75-2/Af |
92.0 |
℃ |
维卡软化温度 |
|
ISO 306/B50 |
102 |
℃ |