规格用途
| 规格级别 |
其它 其它 注塑 |
外观颜色 |
nan |
| 该料用途 |
机械零件汽车部件 |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
nan |
ASTM D-1505 |
0.91 |
克/厘米3 |
| 熔体流动速率 |
nan |
ASTM D-1238 |
0.55 |
克/10分 |
| 相对密度 |
nan |
nan |
0.951 |
nan |
| 熔体流动速率 |
nan |
nan |
21 |
nan |
| 熔体流动速率 |
200℃, 5kg |
ASTM D-1238 |
5.0 |
g/10min |
| 比重 |
nan |
ASTM D-792 |
1.15 |
g/cm3 |
| 成型收缩率 |
nan |
ASTM D-955 |
0.6-0.9 |
% |
| 吸水率 |
24hr,23℃ |
nan |
0.45 |
% |
| 密度 |
|
ISO 1183 |
1.05 |
g/cm3 |
| 熔体流动速率 |
200℃,5kg |
ISO 1133 |
5.0 |
g/10min |
| 吸水率 |
Equilibrium |
ISO 62 |
0.10 |
% |
| 密度 |
nan |
ASTM D-1505 |
0.953 |
g/cm3 |
| 热性能 |
维卡软化点 |
nan |
ASTM D-1525 |
160 |
℃ |
| 热变形温度 |
66磅/英寸2 |
ASTM D-648 |
110 |
℃ |
| 维卡软化点 |
50℃/h 1kg |
ASTM D-1525 |
93 |
℃ |
| 燃烧性 |
nan |
UL-94 |
V-0 |
nan |
| 融点 |
|
DSC |
225 |
℃ |
| 耐燃性 |
0.75mm |
UL94 |
HB |
|
| 热变形温度 |
18.6kg/cm2(4.6kg/cm2) |
ASTM D648 |
60(155) |
℃ |
| 线膨胀系数 |
|
ASTM D696 |
9 |
10-5cm/cm℃ |
| 阻燃等级 |
nan |
UL 94 |
HB |
nan |
| 热变形温度 |
0.45MPa |
ISO 75-2 |
79.0 |
℃ |
| 热变形温度 |
1.80MPa |
ISO 75-2 |
66.0 |
℃ |
| 维卡软化温度 |
50℃/h,B(50N) |
ISO 306 |
85.0 |
℃ |
| CLTE |
Flow |
ISO 11359-2 |
0.000090 |
cm/cm/℃ |
| CLTE |
Transverse |
ISO 11359-2 |
0.000070 |
cm/cm/℃ |
| 熔点 |
nan |
ISO 3146 |
263 |
℃ |
| 热变形温度 |
- |
0.45Mpa |
ISO 75-1/-2 |
205 |
| 热变形温度 |
- |
1.8Mpa |
ISO 75-1/-2 |
72 |
| 脆化温度 |
nan |
ASTM D-746 |
-100 |
℃ |
| 阻燃等级 |
|
UL 94 |
HB |
|
| 维卡软化温度 |
|
ASTM D1525 |
96.0 |
℃ |
| 热变形温度 |
1.8MPa，未退火,4.00mm |
ASTM D-648 |
90.0 |
℃ |
| UL阻燃等级 |
1.60mm |
UL 94 |
HB |
|
| 热变形温度 |
0.45MPa,未退火,4.00mm |
ASTM D-648 |
215 |
℃ |
| 热变形温度 |
1.8MPa,未退火,4.00mm |
ASTM D-648 |
195 |
℃ |
| UL阻燃等级 |
1.6mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火,4.00mm |
ASTM D-648 |
130 |
℃ |
| UL阻燃等级 |
1.60mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8 MPa, 退火, 注塑 |
ASTM D-648 |
95.0 |
℃ |
| 维卡软化温度 |
|
ASTM D-1525 |
109 |
℃ |
| 线形膨胀系数 |
流动 |
ASTM D-696 |
0.000080 |
cm/cm/℃ |
| UL阻燃等级 |
|
UL 94 |
HB |
|
| UL档案号 |
|
|
E57787 |
|
| 热变形温度 |
1.82Mpa |
ASTM D648 |
55 |
℃ |
| 线膨胀系数 |
-30+30℃ |
ASTM D696 |
8.0x10-5 |
1/℃ |
| 燃烧性 |
3.2mm厚 |
UL 94 |
HB |
|
| 机械性能 |
洛氏硬度 |
|
ASTM D-785 |
78 |
M Scale |
| 拉伸模量 |
23℃ |
ASTM D-638 |
3170 |
MPa |
| 抗张屈服强度 |
23℃ |
ASTM D-638 |
52.0 |
MPa |
| 断裂伸长率 |
23℃ |
ASTM D-638 |
3.0 |
% |
| 弯曲模量 |
23℃ |
ASTM D-790 |
3310 |
MPa |
| 弯曲强度 |
23℃ |
ASTM D-790 |
107 |
MPa |
| 悬壁梁缺口冲击强度 |
23℃， 3.18mm |
ASTM D-256 |
20.0 |
J/m |