规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
nan |
| 该料用途 |
用途：包装袋、一般用薄膜包装制品 |
| 备注说明 |
特性：高刚性，高产出。 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
nan |
ASTM D-570 |
>0.01 |
% |
| 密度 |
nan |
ASTM D-792 |
0.956 |
g/cm3 |
| 熔体流动速率 |
nan |
ASTM D-1238 |
0.07 |
g/10min |
| 熔体流动速率 |
nan |
ASTM D-1238 |
0.07 |
g/10min |
| 密度 |
nan |
ASTM D-1505 |
0.956 |
g/cm3 |
| 含水率 |
nan |
ASTM D-570 |
＜0.01 |
% |
| 清洁度 |
nan |
Q/LBB0001-2006 |
3 |
个/kg |
| 熔体流动速率 |
230℃,2.16kg |
GB/T 3682-2000 |
3.2 |
g/10min |
| 等规指数 |
nan |
GB/T 2412-80 |
≥96.9 |
% |
| 粉末灰分 |
A法,800℃ |
GB/T 9345-88 |
≤0.012 |
% |
| 密度 |
nan |
ISO 1183 |
0.94 |
G/cm3 |
| 熔体流动速率 |
230°C/2.16 kg |
ISO 1133 |
4 |
g/10min |
| 热性能 |
比热容 |
nan |
KPIC Method |
0.45 |
cal/g°C |
| 熔点 |
nan |
ASTM D-3418 |
134 |
°C |
| 维卡软化点 |
nan |
ASTM D-1525 |
123 |
°C |
| 热变形温度 |
nan |
ASTM D-648 |
70 |
°C |
| 线性膨胀系数 |
nan |
ASTM D-696 |
1.5 |
10-5cm/cm°C |
| 易变温度 |
nan |
ASTM D-746 |
>-70 |
°C |
| 熔点 |
nan |
ASTM D-3418 |
134 |
℃ |
| 维卡软化点 |
nan |
ASTM D-1525 |
123 |
℃ |
| 热变形温度 |
nan |
ASTM D-648 |
70 |
℃ |
| 低温脆性温度 |
nan |
KPIC Method |
＜-70 |
10-4cal cm/cm sec.℃ |
| 线胀系数 |
nan |
ASTM D-696 |
1.5 |
10-4cm/cm℃ |
| 热度 |
nan |
KPIC Method |
0.45 |
cal/g℃ |
| 维卡软化点 |
nan |
GB/T 1633-2000 |
≥150 |
℃ |
| 维卡软化温度 |
nan |
ISO 306/A50 |
160 |
℃ |
| 热变形温度 |
0.45MPa,未退热 |
ASTM D-648 |
120 |
℃ |
| 热变形温度 |
1.8MPa,未退热 |
ASTM D-648 |
110 |
℃ |
| 维卡软化点 |
|
ISO 306 |
150 |
℃ |