规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
耐热的机械零件和汽车配件 |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 电气性能 |
介电强度 |
3.18mm |
ASTM D-149 |
20 |
kV/mm |
| 介电常数 |
1MHz |
ASTM D-150 |
2.50 |
|
| 物理性能 |
等规度 |
nan |
MPCPP-F-107 |
98 |
% |
| 比重 |
|
ASTM D-792 |
1.04 |
g/cm3 |
| 表观密度 |
|
ASTM D-792 |
0.59-0.64 |
g/cm |
| 表观密度 |
|
ASTM D-792 |
0.62-0.67 |
g/cm |
| 熔体流动速率 |
200℃/5.0kg |
ASTM D-1238 |
3.0 |
g/10min |
| 收缩率 |
流动，23℃ |
ASTM D-955 |
0.40-0.70 |
% |
| 比重 |
|
ASTM D-792 |
1.27 |
g/cm3 |
| 熔流率 |
220℃/10.0kg |
ASTM D-1238 |
27 |
g/10min |
| 收缩率 |
流动,3.20mm |
ASTM D-955 |
0.40-0.60 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
0.30 |
% |
| 比重 |
|
ASTM D-792 |
1.59 |
g/cm3 |
| 收缩率 |
流动,3.20mm |
ASTM D-955 |
0.50-1.0 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
1.4 |
% |
| 比重 |
|
ASTM D-792 |
1.63 |
g/cm3 |
| 收缩率 |
流动,3.20mm |
ASTM D-955 |
0.30-0.50 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
0.060 |
% |
| 比重 |
|
ASTM D-792 |
1.23 |
g/cm3 |
| 收缩率 |
流动,3.20mm |
ASTM D-955 |
0.60-0.90 |
% |
| 比重 |
|
ASTM D-792 |
1.56 |
g/cm3 |
| 收缩率 |
流动,3.20mm |
ASTM D-955 |
0.50-0.60 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
1.4 |
% |
| 比重 |
|
ASTM D792 |
1.42 |
g/cm³ |
| 收缩率 |
流动 (3.18 mm) |
ASTM D955 |
0.30-0.50 |
% |
| 比重 |
|
ASTM D-792 |
1.04 |
g/cm3 |
| 表观密度 |
|
|
0.59 到 0.64 |
g/cm3 |
| 表观密度 |
|
|
0.62 到 0.67 |
g/cm3 |
| 熔流率 |
200℃/5.0 kg |
ASTM D-1238 |
3.0 |
g/10min |
| 收缩率 |
流动, 23℃, 注塑 |
ASTM D-955 |
0.40 到 0.70 |
% |
| 密度 |
|
ISO 1183 |
1.06 |
g/cm³ |
| 表观密度 |
|
ISO 60 |
> 0.50 |
g/cm³ |
| 吸水率 |
饱和, 100℃ 2 |
ISO 62 |
1.7 |
MPa |
| 吸水率 |
饱和, 23℃ 3 |
ISO 62 |
1.2 |
MPa |
| 吸水率 |
平衡, 23℃, 50% RH |
ISO 62 |
0.50 |
MPa |
| 支撑硬度 |
支撐 D |
ISO 868 |
75 |
|
| 球压硬度 |
|
ISO 2039-1 |
101 |
MPa |
| 机械性能 |
洛氏硬度 |
nan |
ASTM D-785 |
100 |
R·度 |
| 抗张屈服应力 |
nan |
ASTM D-638 |
38.0 |
Mpa |
| 挠曲模量 |
nan |
ASTM D-790 |
1700 |
Mpa |
| 抗张强度 |
nan |
ASTM D-638 |
35.0 |
Mpa |
| 断裂伸长率 |
nan |
ASTM D-638 |
500 |
% |
| 螺旋流动长度 |
nan |
MPCPP-A-301 |
45 |
厘米 |
| 拉伸强度 |
nan |
nan |
18 |
MPa |
| 300%定伸应力 |
nan |
nan |
2.4 |
MPa |
| 硬度 |
nan |
nan |
70 |
A度 |
| 扯断永久变形 |
nan |
nan |
40 |
nan |
| 断裂伸长率 |
nan |
nan |
650 |
% |
| 拉伸模量 |
|
ASTM D-638 |
8300 |
MPa |
| 抗张强度 |
|
ASTM D-638 |
85.0 |
MPa |
| 断裂伸长率 |
|
ASTM D-638 |
2.0 |
% |
| 弯曲模量 |
|
ASTM D-790 |
7100 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
129 |
MPa |
| 悬壁梁缺口冲击强度 |
23℃ |
ASTM D-256 |
87 |
J/m |
| 洛氏硬度 |
|
ASTM D-785 |
118 |
R计秤 |
| 拉伸模量 |
|
ASTM D-638 |
9500 |
MPa |
| 抗张强度 |
|
ASTM D-638 |
116 |
MPa |
| 断裂伸长率 |
|
ASTM D-638 |
2.5 |
% |
| 弯曲模量 |
|
ASTM D-790 |
8380 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
181 |
MPa |
| 悬壁梁缺口冲击强度 |
23℃ |
ASTM D-256 |
130 |
J/m |
| 抗张强度 |
|
ASTM D-638 |
70.0 |
MPa |
| 断裂伸长率 |
|
ASTM D-638 |
16 |
% |
| 弯曲模量 |
|
ASTM D-790 |
2910 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
115 |
MPa |
| 悬壁梁缺口冲击强度 |
23℃ |
ASTM D-256 |
180 |
J/m |
| 拉伸模量 |
|
ASTM D-638 |
12200 |
MPa |
| 抗张强度 |
|
ASTM D-638 |
165 |
MPa |
| 断裂伸长率 |
|
ASTM D-638 |
2.2 |
% |
| 弯曲模量 |
|
ASTM D-790 |
8690 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
239 |
MPa |
| 悬壁梁缺口冲击强度 |
23℃ |
ASTM D-256 |
94 |
J/m |
| 拉伸模量 |
|
ASTM D638 |
06890 |
MPa |
| 洛氏硬度 |
M 计秤, 23℃, 注塑 |
ASTM D-785 |
76 |
|
| 拉伸模量 |
23℃, 注塑 |
ASTM D-638 |
3170 |
MPa |
| 抗张屈服强度 |
23℃, 注塑 |
ASTM D-638 |
49.0 |
MPa |
| 断裂伸长率 |
23℃, 注塑 |
ASTM D-638 |
2.0 |
% |
| 弯曲模量 |
23℃, 注塑 |
ASTM D-790 |
3310 |
MPa |
| 弯曲强度 |
23℃, 注塑 |
ASTM D-790 |
100 |