| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 性能 |
拉伸强度 |
ASTM D638 |
|
22.0 152 |
kpsi Mpa |
| 拉伸模量 |
ASTM D638 |
|
650 4.5 |
kpsi GPa |
| 拉伸伸长率 |
ASTM D638 |
|
7.6 |
% |
| 挠曲强度 |
ASTM D790 |
|
34.9 244 |
kpsi Mpa |
| 挠曲模量 |
ASTM D790 |
|
730 5.0 |
kpsi GPa |
| 压缩强度 |
ASTM D695 |
|
32.1 221 |
kpsi Mpa |
| 剪切强度 |
ASTM D732 |
|
18.5 128 |
kpsi Mpa |
| |
悬臂梁式冲击，有缺口 |
ASTM D256 |
|
2.7 140 |
ft-lb/in J/m |
| 悬臂梁式冲击，无缺口 |
ASTM D4812 |
|
20 1060 |
ft-lb/in J/m |
| 热变形温度 |
264psi,ASTM D 648 |
|
278 532 |
℃ ℉ |
| CLTE3 |
ASTM D 696 |
|
31 17 |
ppm/℃丨丨 ppm/℉ |
| 体积电阻率 |
ASTM D 257 |
|
2X107 |
ohm-cm |
| 比重 |
ASTM D 792 |
|
1.42 |
|
| 吸水性，24小时 |
ASTM D 570 |
|
0.33 |
% |
| 摩擦系数，干摩擦50fpm（0.25m/s) |
ASTM D 3702 |
|
0.31 |
|
| 摩擦系数，干摩擦800fpm(4m/s) |
ASTM D 3702 |
|
0.29 |
|
| 摩损系数，干摩擦350fpm（0.25m/s) |
ASTM D 3702 |
|
13 23 |
10-10in3min/ft-lb-hr 10-8mm3/Nm |
| 摩损系数，干摩擦3800fpm(4m/s) |
ASTM D 3702 |
|
18 32 |
10-10in3min/ft-lb-hr 10-8mm3/Nm |
| 摩损系数，润滑环境4 |
ASTM D 3702 |
|
7 12 |
10-10in3min/ft-lb-hr 10-8mm3/Nm |