技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
24hr |
ASTM D-570 |
0.3 |
% |
| 熔体流动速率 |
nan |
ASTM D-1238 |
20.0 |
g/10min |
| 熔体流动速率 |
230°C.3.8kg |
ASTM D-1238 |
2.0 |
g/10min |
| 吸水率 |
24hr |
ASTM D-570 |
0.3 |
% |
| 热性能 |
长期应用温度 |
nan |
nan |
63-77 |
°C |
| 玻璃化温度 |
nan |
ASTM D-3418 |
92 |
°C |
| 维卡软化点 |
nan |
ASTM D-1525 |
77 |
°C |
| 维卡软化点 |
nan |
ASTM D-1525 |
82 |
°C |
| 热变形温度 |
1.86kgf/cm2 |
ASTM D-648 |
77 |
°C |
| 线膨胀系数 |
nan |
ASTM D-696 |
6×10-5 |
cm/cm/°C |
| 热传导系数 |
nan |
ASTM C-177 |
5×10-4 |
cal/s/cm/°C |
| 载荷挠曲温度 |
18.56kg/cm2 |
ASTM D-648 |
102 |
°C |
| 比热 |
nan |
nan |
0.35 |
cal/g/°C |
| 维卡软化点 |
1kg |
ASTM D-1525 |
116 |
°C |
| 机械性能 |
抗压强度 |
|
ASTM D695 |
-- |
MPa |
| 拉伸模量 |
|
ASTM D638 |
-- |
MPa |
| 屈服点拉伸强度 |
|
ASTM D638 |
66.2 |
MPa |
| 弯曲模量 |
|
ASTM D790 |
3030 |
MPa |
| 断裂弯曲强度 |
|
ASTM D790 |
96.5 |
MPa |
| 断裂点伸长率 |
|
ASTM D638 |
-- |
% |
| 缺口冲击强度 |
|
ASTM D256 |
12.3 |
J/m |