规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
片材;带材(薄) |
| 备注说明 |
丙烯聚合物 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
nan |
nan |
0.3 |
g/10min |
| 熔体流动速率 |
nan |
ASTM D-1238L |
0.3 |
g/10min |
| 熔体流动速率 |
nan |
nan |
0.3 |
g/10min |
| 熔体流动速率 |
nan |
ISO 1133 |
0.3 |
g/10min |
| 密度 |
nan |
ISO 1183 |
0.9 |
g/cm3 |
| 熔体流动速率 |
230°C/2.16 kg |
ASTM D1238 |
1.2-1.9 |
g/10min |
| 熔体流动速率 |
230°C/5.0 kg |
ASTM D1238 |
0.3-0.5 |
g/10min |
| 熔体流动速率 |
190°C/5.0 kg |
ASTM D1238 |
0.5-0.9 |
g/10min |
| 熔体流动速率 |
230℃，2.16kg |
ASTM D-1238L |
0.3 |
g/10min |
| 热性能 |
热变形温度 |
0.46N/mm2 |
ASTM D-648 |
90 |
℃ |
| 维卡软化点 |
1kg |
ASTM D-1525 |
152 |
℃ |
| 热变形温度 |
46kg/cm2 |
nan |
90 |
℃ |
| 维卡软化点 |
nan |
nan |
152 |
℃ |
| 维卡软化点 |
nan |
ISO 306/A |
153 |
℃ |
| 热变形温度 |
nan |
ISO 75/B |
100 |
℃ |
| 热变形温度 |
nan |
ASTM D648 |
90-96 |
℃ |
| 维卡软化温度 |
nan |
ISO 306 |
150-154 |
℃ |
| 维卡软化点 |
nan |
ASTM D-1525 |
152 |
℃ |
| 热变形温度 |
0.46N/mm2 |
ASTM D-648 |
90 |
℃ |
| 维卡软化点 |
10N |
|
153 |
℃ |
| 热变形温度 |
|
|
89 |
℃ |
| 热老化 |
150℃ |
|
2250 |
小时 |
| 维卡软化点 |
1kg |
ASTM D-1525 |
152 |
℃ |
| 热变形温度 |
451kPa |
ASTM D-648 |
90 |
℃ |
| 热变形温度 |
0.46MPa |
ISO 75/B |
100 |
℃ |
| 维卡软化点 |
9.8N |
ISO 306/A |
153 |
℃ |