规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
nan |
ASTM D-1238 |
3.2 |
g/10min |
| 熔体流动速率 |
nan |
nan |
3.2 |
g/10min |
| 熔体流动速率 |
nan |
ASTM D-1238 |
3.2 |
g/10min |
| 密度 |
Method D |
ISO 1183 |
0.9 |
G/cm3 |
| 熔体流动速率 |
230°C/2.16 kg |
ISO 1133 |
3 |
g/10min |
| 熔体流动速率 |
230℃，2.16kg |
ASTM D-1238L |
3 |
g/10min |
| 热性能 |
维卡软化点 |
nan |
ASTM D-1525 |
151 |
℃ |
| 热变形温度 |
nan |
nan |
85 |
℃ |
| 热变形温度 |
455Kpa |
ASTM D-648 |
94 |
℃ |
| 热变形温度 |
0.45Mpa, Unannealed |
ISO 75B-1,-2 |
82 |
℃ |
| 热变形温度 |
1.8Mpa, Unannealed |
ISO 75A-1,-2 |
51 |
℃ |
| 维卡软化温度 |
A50 (50°C/h 10N) |
ISO 306 |
155 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
156 |
℃ |
| 热变形温度 |
0.46N/mm2 |
ASTM D-648 |
94 |
℃ |
| 热变形温度 |
0.45MPa,未退火 |
ASTM D-648 |
94 |
℃ |
| 维卡软化点 |
|
ASTM D-1525 |
156 |
℃ |
| 加速干燥箱老化 |
150℃ |
ASTM D-3012 |
360 |
hr |