规格用途
| 规格级别 |
其它 其它 注塑 |
外观颜色 |
nan |
| 该料用途 |
用于大型工业部件和容器类 |
| 备注说明 |
特性：冲击强度、屈服应力、刚性和抗蠕变性优秀 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
nan |
nan |
7.0 |
nan |
| 相对密度 |
nan |
nan |
0.960 |
nan |
| 熔体流动速率 |
300℃/1.2kg |
ASTM D-1238 |
19 |
g/10min |
| 密度 |
nan |
ASTM D-792 |
1.03 |
nan |
| 吸水率 |
nan |
ASTM D-570 |
0.3 |
WT% |
| 比重 |
nan |
ASTM D792 |
1.37 |
g/cm3 |
| 吸水率 |
nan |
ASTM D570 |
0.40 |
% |
| 密度 |
nan |
ASTM D-1505 |
0.965 |
g/cm3 |
| 熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
8.9 |
g/10min |
| 热性能 |
热变形温度 |
未退火@1.82MPa(4mm) |
ASTM D-648 |
115 |
℃ |
| 热变形温度 |
未退火 |
ASTM D-648 |
86 (187) |
℃(F) |
| 维卡软化点 |
nan |
ASTM D-1238 |
100 |
℃ |
| 阻燃等级 |
nan |
UL94 |
HB |
nan |
| 抗热线燃烧性 |
nan |
UL-746A |
15 |
Sece |
| 脆化温度 |
nan |
ASTM D-746 |
-100 |
℃ |
| 热变形温度 |
1.8 MPa, 未退火 |
ASTM D648, ISO 75-2/A |
140 |
℃ |
| 最高连续使用温度 |
|
IEC 60216 |
120 |
℃ |
| 维卡软化温度 |
|
ISO 306/A50, ASTM D1525 |
152 |
℃ |
| 球压测试 |
125℃ |
VDE 0470 |
通过 |
|
| 流动线形膨胀系数 |
-30 到 30℃ |
ASTM D696 |
0.000070 |
cm/cm/℃ |
| UL 阻燃等级 |
1.60 mm |
UL 94 |
V-2 |
|
| 热灯丝点火温度 |
2.00 mm |
IEC 60695-2-13 |
850 |
℃ |
| 极限氧指数 |
|
ASTM D2863 |
26 |
% |
| 玻璃转化温度 |
DSC |
Internal Method |
-14.0 |
℃ |
| 维卡软化温度 |
|
ASTM D1525 |
105 |
℃ |
| 溶融温度 |
DSC |
Internal Method |
108 |
℃ |