品名： HDPE 牌号：H5618 厂家：量子化学
规格用途| 规格级别 | 增韧,热稳定 其它 注塑 | 外观颜色 | nan |
| 该料用途 | 家庭用品，集装箱 | ||
| 备注说明 | 加工性能好，韧性好，气味低，加工稳定性好 | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 密度 | ASTM D-1505 | 0.956 | g/cm3 | |
| 熔体流动速率 | ASTM D-1238 | 18 | g/10min | ||
| 密度 | nan | ASTM D-1505 | 0.956 | g/cm3 | |
| 表观密度 | nan | ASTM D-1895 | 0.53-0.59 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 18 | g/10min | |
| 机械性能 | 拉伸模量 | ASTM D-638 | 1050 | MPa | |
| 屈服拉伸强度 | ASMT D-638 | 29.2 | MPa | ||
| 断裂拉伸强度 | ASTM D-638 | 24 | MPa | ||
| 屈服伸长率 | ASTM D-638 | 8.0 | % | ||
| 断裂伸长率 | ASTM D-638 | 62 | % | ||
| 弯曲模量 | ASTM D-790 | 1490 | MPa | ||
| 缺口冲击强度 | ASTM D-256 | 31 | J/m | ||
| 硬度 | ASTM D-2240 | 69 | |||
| 拉伸模量 | nan | ASTM D-638 | 1050 | MPa | |
| 拉伸模量 | 1% Secant | ASTM D-638 | 845 | MPa | |
| 拉伸屈服强度 | nan | ASTM D-638 | 29.2 | MPa | |
| 拉伸断裂强度 | nan | ASTM D-638 | 24 | MPa | |
| 屈服伸长率 | nan | ASTM D-638 | 8 | % | |
| 断裂伸长率 | nan | ASTM D-638 | 62 | % | |
| 弯曲模量 | nan | ASTM D-790 | 1490 | MPa | |
| 弯曲模量 | 1% Secant | ASTM D-790 | 1410 | MPa | |
| 弯曲模量 | 2% Secant | ASTM D-790 | 1180 | MPa | |
| 悬臂梁缺口冲击强度 | 23℃ | ASTM D-256 | 31 | J/m | |
| 悬臂梁冲击强度 | -18℃ | ASTM D-4812 | NO Break | nan | |
| 热性能 | 脆化温度 | ASTM D-746 | ＜-76.1 | ℃ | |
| 维卡软化点 | ASTM D-1525 | 124 | ℃ | ||
| 熔点 | ASTM D-3418 | 130 | ℃ | ||
| 邵氏硬度 | nan | ASTM D-2240 | 69 | nan | |
| 热变形温度 | 0.45MPa,未退火 | ASTM D-648 | 72.8 | ℃ | |
| 脆化温度 | nan | ASTM D-746 | ＜-76.1 | ℃ | |
| 维卡软化点 | nan | ASTM D-1525 | 124 | ℃ | |
| 熔融温度 | nan | ASTM D-3418 | 130 | ℃ | |
| DSC | nan | ASTM D-3418 | 115 | ℃ |