规格用途
| 规格级别 |
其它 其它 均聚注塑 |
外观颜色 |
nan |
| 该料用途 |
汽车部件及家具等 |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
nan |
ASTM D-1238 |
3.0 |
g/10min |
| 密度 |
nan |
ASTM D-1505 |
0.91 |
g/cm3 |
| 密度 |
nan |
ASTM D-1505 |
0.924 |
g/cm3 |
| 熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
8.0 |
g/10min |
| 比重 |
nan |
ASTM D792 |
1.37 |
g/cm³ |
| 熔体流动速率 |
385℃/2.16 kg |
ASTM D1238 |
80 |
g/10 min |
| 成型收缩率 |
flow,3.20mm |
ASTM D955 |
0.70 |
% |
| 吸水性 |
23℃24h |
ASTM D570 |
0.54 |
% |
| 热性能 |
维卡软化点 |
nan |
ASTM D-1525 |
160 |
℃ |
| 热变形温度 |
66磅/英寸² |
ASTM D-648 |
110 |
℃ |
| 脆化温度 |
nan |
ASTM D-746 |
-75 |
℃ |
| 维卡软化点 |
nan |
ASTM D-1525 |
95 |
℃ |
| 热变形温度 |
1.8Mpa,未退火 |
ASTM D648 |
203 |
℃ |
| 线性热膨胀系数 |
flow |
ASTM E831 |
0.000049 |
cm/cm/°C |
| 热变形温度 |
1.8 MPa, 未退火 |
ASTM D648 |
78.3 |
℃ |
| 阻燃等级 |
|
UL 94 |
HB |
|
| 热变形温度 |
0.45MPa,未退火,4.00mm |
ASTM D-648 |
230 |
℃ |
| 热变形温度 |
1.8MPa,未退火,4.00mm |
ASTM D-648 |
215 |
℃ |
| UL阻燃等级 |
1.6mm |
UL 94 |
HB |
|
| 热变形温度 |
0.45MPa，未退火,4.00mm |
ASTM D-648 |
100 |
℃ |
| 热变形温度 |
1.8MPa，未退火,4.00mm |
ASTM D-648 |
98.0 |
℃ |
| UL阻燃等级 |
1.60mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火,4.00mm |
ASTM D-648 |
98.0 |
℃ |
| UL阻燃等级 |
1.60mm |
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，未退火,4.00mm |
ASTM D-648 |
140 |
℃ |
| UL阻燃等级 |
1.60mm |
UL 94 |
HB |
|