品名： HDPE 牌号：5305E 厂家：韩国韩洋
规格用途| 规格级别 | 其它 其它 挤出 | 外观颜色 | nan |
| 该料用途 | 用途：电线涂层 | ||
| 备注说明 | 特性：优良的电线外观、高速加工性 | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 密度 | nan | ASTM D-1505 | 0.948 | g/cm3 |
| 熔体流动速率 | nan | ASTM D-1238 | 0.8 | g/10min | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.8 | g/10min | |
| 密度 | nan | ASTM D-1505 | 0.952 | g/cm3 | |
| 熔体流动速率 | nan | ISO 1133 | 0.80 | g/10min | |
| 密度 | nan | ISO 1183 | 951 | kg/m3 | |
| 机械性能 | 冲击强度 | nan | ASTM D-256 | 15 | kg·cm/cm |
| 最终拉伸率 | nan | ASTM D-638 | 800 | % | |
| 耐环境应力破裂 | nan | ASTM D-1693 | >1,000 | F50hr | |
| 断裂拉伸强度 | nan | ASTM D-638 | 230 | Kg/cm2 | |
| 挠曲强度 | nan | ASTM D-747 | 6,000 | Kg/cm2 | |
| 屈服拉伸强度 | nan | ASTM D-638 | 250 | Kg/cm2 | |
| 洛氏硬度 | nan | ASTM D-785 | 50 | R | |
| 断裂抗拉强度 | nan | ASTM D-638 | 260 | kg/cm2 | |
| 最终伸长量 | nan | ASTM D-638 | ＞800 | % | |
| 环境抗裂 | 50℃ | ASTM D-1693 | ＞2000 | R | |
| 屈服点应力 | nan | ISO 527-2 | 24 | MPa | |
| 断裂伸长率 | nan | ISO 527-2 | 440 | % | |
| 抗拉伸弹性系数 | nan | ISO 527-1 | 1100 | MPa | |
| 弯曲弹性率 | nan | ISO 178 | 1000 | MPa | |
| 摆锤冲击强度 | nan | ISO 179-1 | 6 | KJ/m2 | |
| D型肖氏硬度 | nan | ISO 868 | 62 | nan | |
| 耐环境应力开裂性 | nan | ASTM D-1693 | ＞600 | hours | |
| 热性能 | 维卡软化点 | nan | ASTM D-1525 | 122 | C° |
| 熔点 | nan | ASTM D-2117 | 130 | C° | |
| 脆化温度 | nan | ASTM D-746 | <-80 | C° | |
| 维卡软化点 | nan | ISO 306 | 122 | ℃ | |
| 融点 | nan | ISO 11357-3 | 130 | ℃ |