品名： HDPE 牌号：1000 厂家：美国霍尼韦尔
规格用途| 规格级别 | 其它 其它 注塑 | 外观颜色 | nan |
| 该料用途 | 家用器皿用 | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 相对密度 | nan | nan | 0.960 | nan |
| 熔体流动速率 | nan | nan | 20 | nan | |
| 熔体流动速率 | nan | nan | 30 | nan | |
| 相对密度 | nan | nan | 0.917 | nan | |
| 吸水率 | 平衡,73℉ | ASTM D-570 | 1.25 | % | |
| 吸水率 | 24小时，73℉ | ASTM D-570 | 0.250 | % | |
| 熔体流动速率 | ASTM D-1238 | 8.9 | g/10min | ||
| 降伏点抗张强度 | 23℃ | ASTM D-638 | 430 | kg/cm2 | |
| 降伏点抗张强度 | 23℃ | ASTM D-638 | 6100 | psi | |
| 断裂点抗张强度 | 1/8" | ASTM D-638 | 350 | kg/cm2 | |
| 断裂点抗张强度 | 1/8" | ASTM D-638 | 5000 | psi | |
| 断裂拉伸率 | 1/8" | ASTM D-638 | 30 | % | |
| 抗折强度 | 23℃ 2.8mm/min | ASTM D-790 | 700 | kg/cm2 | |
| 抗折强度 | 23℃ 2.8mm/min | ASTM D-790 | 10000 | psi | |
| 抗折系数 | 23℃ 2.8mm/min | ASTM D-790 | 24000 | kg/cm2 | |
| 抗折系数 | 23℃ 2.8mm/min | ASTM D-790 | 340000 | psi | |
| 密度 | ASTM D-792 | 1.03 | |||
| 吸水率 | ASTM D-570 | 0.3 | WT% | ||
| 熔体流动速率 | 200℃/5.0kg | ASTM D-1238 | 3.5 | g/10min | |
| 密度 | nan | ASTM D-1505 | 0.955 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.33 | g/10min | |
| 熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 29 | g/10min | |
| 比重 | nan | ASTM D792 | 9.98 | g/cm3 | |
| 成型收缩率 | nan | ASTM D955 | 0.40 | % | |
| 吸水率 | nan | ASTM D570 | 0.02 | % | |
| 物理性能 | 密度 | ASTM D792 | 1.31 | ||
| 收缩率 | 平行流动方向（3.18 mm） | ASTM D955 | 0.018 | cm/cm | |
| 24小时吸水率 | ASTM D570 | 0.08 | % | ||
| 热性能 | 热指数 | 电性能 | UL746B | 170 | |
| 热指数 | 机械冲击性能 | UL746B | 170 | ||
| 热指数 | 非机械性能 | UL746B | 170 | ||
| 维卡软化点 | ASTM D-1525 | 426 | ℉ | ||
| 线膨胀系数 | flow | ASTM E-831 | 3 | ||
| 线膨胀系数 | xflow | ASTM E-831 | 3 | ||
| 燃烧性 | UL 94 | 5VA | class | ||
| 热变形温度 | 264Psi | ASTM D-648 | 392 | ℉ | |
| 热变形温度 | 66Psi | ASTM D-648 | 410 | ℉ | |
| 热变形温度 | 未退火 | ASTM D-648 | 87（189） | ℃(F) | |
| 维卡软化点 | ASTM D-1525 | 102 | ℃ | ||
| 阻燃等级 | UL94 | HB | |||
| 抗热线燃烧性 | UL-746A | 17 | Sece | ||
| 熔点 | nan | ISO 3146 | 263 | ℃ | |
| 热变形温度 | - | 1.8Mpa | ISO 75-1/-2 | 72 | |
| 热变形温度 | - | 0.45Mpa | ISO 75-1/-2 | 205 | |
| 热变形温度 | 1.80MPa，未退火，3.18mm | ASTM D-648 | 78.0 | ℃ | |
| 热变形温度 | 1.80MPa，退火，3.18mm | ASTM D-648 | 92.8 | ℃ | |
| 维卡软化温度 | nan | ASTM D-1525 | 104 | ℃ | |
| 阻燃性 | 1.59mm | UL 94 | HB | nan | |
| 热变形温度 | - | 0.45Mpa,未退火 | ISO 75-2/B | 150 | |
| 热变形温度 | - | 1.8Mpa,未退火 | ISO 75-2/B | 55 | |
| 维卡软化温度 | - | nan | ISO 306/A | 220 | |
| 维卡软化温度 | - | nan | ISO 306/B | 180 | |
| 熔化温度 | nan | nan | 221-226 | ℃ | |
| 阻燃性 | - | 0.8mm | UL94 | HB | |
| 阻燃性 | - | 1.6mm | UL94 | HB | |
| 阻燃等级 | 1.52 mm | UL 94 | HB | nan | |
| 热变形温度 | 0.45MPa，未退火 | ASTM D-648 | 74.0 | ℃ | |
| 脆化温度 | nan | ASTM D-746 | -76.0 | ℃ | |
| 维卡软化温度 | nan | ASTM D-1525 | 128 | ℃ | |
| CLTE | nan | ASTM D-696 | 0.00013 | cm/cm/℃ | |
| 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 150 | ℃ | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 55.0 | ℃ | ||
| 维卡软化温度 | -- | ISO 306/A | 220 | ℃ | |
| -- | ISO 306/B | 180 | ℃ | ||
| 熔融温度 | ISO 11357-3 | 221 到 226 | ℃ | ||
| 线形膨胀系数 | 流动 : 23 到 55℃ | ISO 11359-2 | 0.00011 | cm/cm/°℃ | |
| 横向 : 23 到 55℃ | ISO 11359-2 | 0.00011 | cm/cm/℃ | ||
| 其他 | 透气率 | 25℃，10μm，0%RH | ASTM D-3985 | 1.7 | cm3mm/m2/atm/24hr |