品名： GPPS 牌号：500 厂家：爱彼斯
规格用途| 规格级别 | 其它 其它 其它 | 外观颜色 | nan |
| 该料用途 | 医用包装、实验室试验物品、化装品包装、绝缘、电器包装、CD盒、照明器材、无线电部件、显示器等。 | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 加工性能 | 成型方法 | nan | Method | 注塑 | nan |
| 物理性能 | 比重 | nan | ISO:1183/1987 | 1.04 | nan |
| 吸水量 | 浸泡均衡点+73℉(+23℃) | ASTM D-570 | 0.90 | % | |
| 吸水量 | Equil.50%R.h.+73℉(+23℃) | ASTM D-570 | 0.22 | % | |
| 挠曲系数 | +70℃ | 在25℃下 | 1585 | MPa | |
| 吸水量 | 24hrs浸泡+73℉(+23℃) | ASTM D-570 | 0.25 | % | |
| 溶融流动指数 | 12-14 | g/10min | |||
| 比重 | nan | ASTM D-792 | 1.04 | nan | |
| 比重 | 23℃ | ASTM D-792 | 1.05 | nan | |
| 模具收缩率 | nan | nan | 0.4-0.6 | % | |
| 缩模率 | nan | ASTM D-955 | 0.4-0.6 | % | |
| 熔融指数 | 300℃，1.2kg | ASTM D-1238 | 20 | g/10min | |
| 比重 | nan | ASTM D-792 | 1.07 | g/cm3 | |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.30-0.70 | % | |
| 比重 | nan | ASTM D-792 | 1.05 | g/cm3 | |
| 模具收缩率 | nan | ISO 294-4 | 0.40-0.70 | % | |
| 密度 | ISO 1183 | 1.17 | g/cm3 | ||
| 比重 | ASTM D-792 | 1.42 | |||
| 熔体流动速率 | ASTM D-1238 | 12 | g/10min | ||
| 收缩率 | 1/8" Section | 2.1 | % | ||
| 密度 | g/cm³ | 1.19 | ℃ | ||
| 密度 | ISO 1183 | 1.13 | g/cm³ | ||
| 密度 | ISO 1183/C | 1.76 | g/cm3 | ||
| 熔体流动速率 | 230℃/21.6 kg | ISO 1133 | 4 | g/10 min | |
| 吸水率 | 24 hr | ASTM D570 | 0.04 | % | |
| 比重 | ASTM D792 | 1.05 | g/cm³ | ||
| 密度 | ISO 1183 | 1.19 | g/cm³ | ||
| 熔流率 | 230℃/5.0 kg | ISO 1133 | 2.0 | g/10 min | |
| 比重 | 1.04 | g/cm3 | |||
| 熔流率 | 200℃/5.0 kg | ASTM D1238 | 14 | g/10min | |
| 收缩率 | 流动 | ASTM D955 | 0.40 到 0.70 | % | |
| 吸水率 | 24hr | <0.1 | % | ||
| 比重 | ASTM D792 | 1.15 | g/cm3 | ||
| 比重 | ASTM D792 | 0.860 | g/cm3 | ||
| 门尼粘度 | ML 1+4, 125℃ | ASTM D1646 | 51到 61 | MU | |
| 亚乙基-降冰片烯含量 | Internal Method | 2.0 | wt% | ||
| 比重 | ASTM D792 | 1.56 | g/cm3 | ||
| 流动收缩率 | ASTM D955 | 0.20 | % | ||
| 吸水率 | 24hr | ASTM D570 | 0.70 | % | |
| 洛氏硬度 | R计秤 | ASTM D785 | 121 | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | 23℃, 3.18 mm | ASTM D256 | 220 | J/m |
| 机械性能 | 摩擦系数 | +73℉(+23℃)动态 | ThrustWasherTest3 | 0.35 | nan |
| 挠曲系数 | +23℃ | 在25℃下 | 2830 | MPa | |
| 剪力 | +23℃ | ASTM D-732 | 65.5 | MPa | |
| 剪力 | +73℉ | ASTM D-732 | 9.5 | MPsi | |
| 挠曲系数 | -55℃ | 在25℃下 | 3930 | MPa | |
| 洛氏硬度 | nan | ASTM D-785 | M94,R120 | nan | |
| 弯曲疲劳忍耐限度 | +73℉ | ASTM D-671 | 4.5 | MPsi | |
| 拉力冲击抵抗力 | +73℉ | ASTM D-1822 | 100 | ft.lb/in2 | |
| 扩散因数 | +73℉(+23℃)106Hz | ASTM D-150 | 0.005 | nan | |
| 伸张强度 | +158℉ | ASTM D-638 | 6.9 | MPsi | |
| 弯曲降服强度 | +73℉ | ASTM D-790 | 14.1 | MPsi | |
| 伸张强度 | +70℃ | ASTM D-638 | 47.5 | MPa | |
| IZOD冲击强度 | 40℃ | ASDM D-256 | 64.1 | j/m | |
| 伸张强度 | +100℃ | ASTM D-638 | 35.9 | MPa | |
| 断裂时之拉力伸张度 | +73℉(+23℃) | ASTM D-638 | 40 | % | |
| 伸张强度 | +212℉ | ASTM D-638 | 5.2 | MPsi | |
| 断裂时之拉力伸张度 | +250℉(+122℃) | ASTM D-638 | >260 | % | |
| 压缩应力 | +73℉@1%Def. | ASTM D-695 | 5.2 | MPsi | |
| 挠曲系数 | +158℉ | 在25℃下 | 230 | MPsi | |
| 无切口冲击程度 | +23℃ | ASDM D-256 | 1280 | j/m | |
| IZOD冲击强度 | +23℃ | ASTM D-256 | 74.7 | j/m | |
| 拉力冲击抵抗力 | +23℃ | ASTM D-1822 | 200 | kj/m2 | |
| 断裂时之拉力伸张度 | +212℉(+100℃) | ASTM D-638 | >260 | % | |
| IZOD冲击强度 | +73℉ | ASDM D-256 | 1.4 | ft.lb/in | |
| 压缩应力 | +23℃@10%Def. | ASTM D-695 | 124 | MPa | |
| 断裂时之拉力伸张度 | -68℉(-55℃) | ASTM D-638 | 13 | % | |
| 挠曲系数 | +212℉ | 在25℃下 | 90 | MPsi | |
| 伸张强度 | -68℉ | ASTM D-638 | 14.7 | MPsi | |
| 熔点 | nan | ASTM D-2133 | 175 | ℃ | |
| 无切口冲击程度 | +73℉ | ASDM D-256 | 24 | ft.lb/in | |
| 弹性系数 | +23℃ | ASTM D-638 | 3100 | MPa | |
| 弯曲疲劳忍耐限度 | +23℃ | ASTM D-671 | 31.0 | MPa | |
| 伸张强度 | -55℃ | ASTM D-638 | 101 | MPa | |
| 弹性系数 | +73℉ | ASTM D-638 | 450 | MPsi | |
| 负载下之变形 | 2000psi@+122℉(14MPa@50℃) | ASTM D-621 | 0.5 | % | |
| 挠曲系数 | +73℉ | 在25℃下 | 410 | MPsi | |
| 伸张强度 | +122℃ | ASTM D-638 | 26.2 | MPa | |