规格用途
| 规格级别 |
阻燃 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
线圈骨架、家电底座、配线器、照明设备零件等 |
| 备注说明 |
特生：阻燃、矿物增强 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
200℃/5.0kg |
ASTM D-1238 |
1.4 |
g/10min |
| 电气性能 |
体积电阻率 |
|
ASTM D-257 |
1.0E+17 |
ohm·cm |
| 介电强度 |
|
ASTM D-149 |
15 |
kV/mm |
| 介电常数 |
50Hz |
ASTM D-150 |
3.0 |
|
| 介电常数 |
1MHz |
ASTM D-150 |
2.9 |
|
| 耗散因素 |
50Hz |
ASTM D-150 |
0.00090 |
|
| 耗散因素 |
1MHz |
ASTM D-150 |
0.010 |
|
| 耐电弧性 |
1.59mm |
|
120 |
sec |
| 机械性能 |
洛氏硬度 |
|
ASTM D-785 |
70 |
|
| 拉伸模量 |
|
ASTM D-638 |
2400 |
MPa |
| 拉伸屈服强度 |
|
ASTM D-638 |
60 |
MPa |
| 拉伸断裂强度 |
|
ASTM D-638 |
70 |
MPa |
| 屈服伸长率 |
|
ASTM D-638 |
7 |
% |
| 断裂伸长率 |
|
ASTM D-638 |
100 |
% |
| 弯曲模量 |
|
ASTM D-790 |
2400 |
MPa |
| 弯曲强度 |
屈服 |
ASTM D-790 |
95 |
MPa |
| 悬臂梁缺口冲击强度 |
23℃，3.2mm |
ASTM D-256 |
700 |
J/m |
| 热性能 |
阻燃性 |
|
UL 94 |
V0 |
|
| 热变形温度 |
0.45MPa |
ASTM D-648 |
120 |
℃ |
| 热变形温度 |
0.45MPa |
ASTM D-648 |
100 |
℃ |
| 阻燃性 |
nan |
UL 94 |
V0 |
nan |
| 热变形温度 |
1.80MPa，未退火 |
ASTM D-648 |
93.3 |
℃ |
| 维卡软化温度 |
nan |
ASTM D-1525 |
107 |
℃ |
| |
阻燃性 |
UL94 |
HB |
|
| 熔融温度 |
|
ASTM D3418 |
155-160 |
℃ |
| 热变形温度 |
1.8 MPa, 未退火 |
ASTM D648 |
73.9 |
℃ |
| 熔融温度 |
|
ASTM D3418 |
216 |
℃ |
| 物理性能 |
比重 |
|
ASTM D-792 |
1.2 |
g/cm3 |
| 熔流率 |
300℃/1.2kg |
ASTM D-1238 |
17 |
g/10min |
| 收缩率 |
流动 |
ASTM D-955 |
0.5-0.7 |
% |
| 吸水率 |
24hr |
|
0.15 |
% |
| 吸水率 |
饱和 |
|
0.35 |
% |
| 机械性能 |
拉伸强度 |
|
ASTM D638 |
96.5 |
MPa |
| 拉伸模量 |
|
ASTM D638 |
4830 |
MPa |
| 弯曲模量 |
|
ASTM D790 |
4480 |
MPa |
| 弯曲强度 |
|
ASTM D790 |
145 |
MPa |
| 断裂点伸长率 |
|
ASTM D638 |
3.5 |
% |
| 缺口冲击强度 |
3.18 mm |
ASTM D256 |
53.4 |
J/m |
| 非缺口冲击强度 |
3.18 mm |
ASTM D256 |
374 |
J/m |