规格用途
| 规格级别 |
其它 其它 注塑 |
外观颜色 |
nan |
| 该料用途 |
注塑级制品 |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
nan |
nan |
9 |
nan |
| 相对密度 |
nan |
nan |
0.950 |
nan |
| 密度 |
|
ISO 1183 |
1050 |
kg/m3 |
| 熔体质量流动速率 |
230℃,3.8kg |
ASTM D-1238 |
0.30 |
g/10min |
| 熔体体积流率 |
220℃,10kg |
ISO 1133 |
3.50 |
cm3/10min |
| 熔体流动速率 |
220℃/10.0kg |
ISO 1133 |
18 |
g/10min |
| 熔体流动速率 |
265℃/5.0kg |
ASTM D-1238 |
30 |
g/10min |
| 热性能 |
熔点 |
nan |
nan |
473 |
℉ |
| 阻燃性 |
nan |
IEC 1210 |
HB |
nan |
| 热变形温度 |
18.6kg/cm2 |
ASTM D648 |
100 |
℃ |
| 热膨胀系数 |
nan |
ASTM D696 |
8.3×10-5 |
mm/mm/℃ |
| 阻燃性 |
nan |
UL94 |
HB |
nan |
| 热变形温度 |
0.45MPa，未退火，3.18mm |
ASTM D-648 |
92.2 |
℃ |
| 热变形温度 |
1.80MPa，未退火，3.18mm |
ASTM D-648 |
84.4 |
℃ |
| CLTE |
|
ASTM D-696 |
0.000094 |
cm/cm℃ |
| 燃烧性 |
1.57mm |
UL 94 |
HB |
|
| 热变形温度 |
0.45MPa，未退火 |
ASTM D-648 |
91.0 |
℃ |
| 燃烧性 |
|
UL 94 |
HB |
|
| 热变形温度 |
1.8MPa，Unannealed，6.35mm |
ASTM D-648 |
103 |
℃ |
| 热变形温度 |
1.8MPa，Annealed，6.35mm |
nan |
121 |
℃ |
| 维卡软化点 |
nan |
ASTM D-1525 |
137 |
℃ |
| 热变形温度 |
ASTM D648 |
0.45MPa，未退火 |
221 |
℃ |
| 最高连续使用温度 |
|
ASTM D794 |
80.0 |
℃ |
| 脆化温度 |
|
ASTM D746 |
-30.0 |
℃ |
| 热变形温度 |
66 psi, 未退火 |
ASTM D648 |
/ |
°F |
| 热变形温度 |
1.8 MPa, 未退火 |
ISO 75-2/A |
105 |
℃ |
| 线形膨胀系数 - 流动 |
|
ISO 11359-2 |
1.1E-4 |
cm/cm/℃ |
| RTI Imp |
3.00 mm |
UL 746 |
90.0 |
℃ |
| UL 阻燃等级 |
3.00 mm |
ISO 1210 |
HB |
|