规格用途
| 规格级别 |
其它 其它 注塑 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
230℃,2.16kg |
ASTM D-1238L |
2 |
g/10min |
| 密度 |
nan |
ASTM D-1505 |
0.9 |
g/cm3 |
| 熔体流动速率 |
230℃，2.16kg |
|
1.8 |
g/10min |
| 密度 |
|
ASTM D-792 |
0.90 |
g/cm3 |
| 熔体流动速率 |
230℃/2.16kg |
ISO 1133 |
2 |
g/10min |
| 密度 |
|
ISO 1183 |
0.9 |
g/cm3 |
| 熔体流动速率 |
230℃,2.16kg |
ASTM D-1238L |
2.0 |
g/10min |
| 密度 |
nan |
ASTM D-1505 |
0.9 |
g/cm3 |
| 熔体流动速率 |
230°C/2.16 kg |
ASTM D1238 |
1.8 |
g/10min |
| 熔体流动速率 |
230°C/2.16 kg |
ASTM D1238 |
1.8 |
g/10min |
| 热性能 |
维卡软化点 |
nan |
ASTM D-1525 |
150 |
℃ |
| 热变形温度 |
|
ASTM D-648 |
88 |
℃ |
| 热变形温度 |
0.45MPa |
ISO 75/B |
80 |
℃ |
| 热变形温度 |
0.46N/mm2 |
ASTM D-648 |
110 |
℃ |
| 负荷弯曲温度 |
0.45Mpa, Unannealed |
ASTM D648 |
88 |
℃ |
| 负荷弯曲温度 |
0.45Mpa, Unannealed |
ASTM D648 |
88 |
℃ |
| 热变形温度 |
0.45MPa |
GB/T 1634.1-2004 |
71 |
℃ |