规格用途
| 规格级别 |
其它 其它 注塑 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 机械性能 |
洛氏硬度 |
|
ASTM D-785 |
100 |
R-Scale |
| 拉伸屈服强度 |
|
ASTM D-638 |
40.7 |
MPa |
| 拉伸断裂伸长率 |
|
ASTM D-638 |
3.1 |
% |
| 弯曲模量 |
|
ASTM D-790 |
2340 |
MPa |
| 弯曲强度 |
|
ASTM D-790 |
71.0 |
MPa |
| IZOD缺口冲击强度 |
23℃，3.18mm |
ASTM D-256 |
256 |
J/m |
| 洛氏硬度 |
R-Scale |
ASTM D-785 |
118 |
|
| 拉伸强度 |
|
ASTM D-638 |
55.2 |
MPa |
| 拉伸屈服伸长率 |
|
ASTM D-638 |
88 |
% |
| 弯曲模量 |
|
ASTM D-790 |
228 |
MPa |
| 弯曲屈服强度 |
|
ASTM D-790 |
89.6 |
MPa |
| 悬臂梁缺口冲击强度 |
3.18mm |
ASTM D-256 |
641 |
J/m |
| 电气性能 |
表面电阻率 |
|
ASTM D-257 |
1.0E+14 |
ohms |
| 体积电阻率 |
|
ASTM D-257 |
1.0E+15 |
ohm·cm |
| 介电强度 |
|
ASTM D-149 |
28 |
kV/mm |
| 表面电阻率 |
|
ASTM D-257 |
1.0E+16 |
ohms |
| 体积电阻率 |
|
ASTM D-257 |
1.0E+17 |
ohm·cm |
| 介电强度 |
|
ASTM D-149 |
17 |
kV/mm |
| 物理性能 |
成型收缩率 |
nan |
ASTM D-955 |
1.5-2.0 |
% |
| 比重 |
|
ASTM D-792 |
1.23 |
g/cm3 |
| 模具收缩率 |
Flow |
ASTM D-955 |
0.40 |
% |
| 熔体流动速率 |
230℃/3.8kg |
ASTM D-1238 |
5.0 |
g/10min |
| 吸水率 |
24hr |
ASTM D-570 |
0.30 |
% |
| 比重 |
|
ASTM D-792 |
1.15 |
g/cm3 |
| 模具收缩率 |
Flow(3.18mm) |
ASTM D-955 |
0.45 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
0.050 |
% |
| 成型收缩率-Flow |
3.18mm |
ASTM D-955 |
0.7 |
% |
| 成型收缩率-Flow |
3.18mm |
ASTM D-955 |
0.6 |
% |
| 比重 |
|
ASTM D792 |
1.42 |
g/cm³ |
| 密度 |
|
ISO 1183 |
1.30 |
g/cm3 |
| 硬度 |
邵氏 A |
ISO 868 |
60 |
|
| 密度 |
|
ISO 1183 |
1.25 |
g/cm3 |
| 硬度 |
邵氏 A |
ISO 868 |
71 |
|
| 密度 |
|
ISO 1183 |
1.26 |
g/cm3 |
| 硬度 |
邵氏 A |
ISO 868 |
65 |
|
| 密度 |
|
ISO 1183 |
1.35 |
g/cm3 |
| 硬度 |
邵氏 A |
ISO 868 |
67 |
|
| 密度 |
|
ISO 1183 |
1.29 |
g/cm3 |
| 硬度 |
邵氏 A |
ISO 868 |
70 |
|
| 比重 |
|
ASTM D792 |
1.46 |
g/cm³ |
| 熔流率 |
230℃/2.16 kg |
ASTM D1238 |
10-15 |
g/10 min |
| 流动收缩率 |
3.18 mm |
ASTM D955 |
1.0-1.2 |
% |
| 流动收缩率 |
6.35 mm |
ASTM D955 |
1.2-1.4 |
% |
| 吸水率 |
24 hr |
ASTM D570 |
0.020 |
% |
| 洛氏硬度 |
R 计秤 |
ASTM D785 |
90-95 |
|
| 机械性能 |
拉伸强度 |
nan |
ASTM D-638 |
48 |
MPa |
| 弯曲强度 |
nan |
ASTM D-790 |
105 |
MPa |
| 弯曲模量 |
nan |
ASTM D-790 |
2000 |
MPa |
| 悬臂梁缺口冲击强度 |
3.2mm宽 |
ASTM D-256 |
69 |
J/m |
| 简支梁无缺口冲击强度 |
nan |
ISO 179 |
>100 |
KJ/m2 |
| 简支梁缺口冲击强度 |
nan |
ISO 179 |
20 |
KJ/m2 |
| 拉伸强度 |
|
ASTM D638 |
200 |
MPa |
| 拉伸断裂伸长率 |
|
ASTM D638 |
200 |
% |
| 弯曲模量 |
|
ASTM D790 |
965 |
MPa |
| 弯曲强度 |
|
ASTM D790 |
28.3 |
MPa |
| IZOD缺口冲击强度 |
3.18mm |
ASTM D256 |
53.4 |
J/m |
| 抗张强度 |
|
ASTM D638 |
56.5 |
MPa |
| 拉伸应力 |
断裂 |
ISO 527-2 |
> 12.0 |
MPa |
| 拉伸应变 |
断裂 |
ISO 527-2 |
> 380 |
% |
| 拉伸应力 |
断裂 |
ISO 527-2 |
> 12.0 |
MPa |
| 拉伸应变 |
断裂 |
ISO 527-2 |
> 280 |
% |
| 拉伸应力 |
断裂 |
ISO 527-2 |
> 14.0 |
MPa |
| 拉伸应变 |
断裂 |
ISO 527-2 |
> 340 |
% |
| 拉伸应力 |
断裂 |
ISO 527-2 |
> 12.0 |
MPa |
| 拉伸应变 |
断裂 |
ISO 527-2 |
> 260 |
% |
| 拉伸应力 |
断裂 |
ISO 527-2 |
> 12.0 |
MPa |
| 拉伸应变 |
断裂 |
ISO 527-2 |
> 280 |
% |
| 拉伸模量 |
23℃ |
ASTM D638 |
3100 |
MPa |
| 抗张强度 |
23℃ |
ASTM D638 |
24.8 |
MPa |
| 屈服伸长率 |
23℃ |
ASTM D638 |
5.0 |
% |
| 弯曲模量 |
正切23℃ |
ASTM D790 |
2900 |
MPa |
| 弯曲强度 |
23℃ |
ASTM D790 |
37.9 |
MPa |
| 悬壁梁缺口冲击强度 |
23℃，3.18 mm |
ASTM D256 |
16 |
J/m |
| 热性能 |
热变形温度 |
1.8 MPa, 未退火 |
ASTM D648 |
71.1 |
°C |
| 基本性能 |
密度 |
nan |
ASTM D-792 |
1.1 |
g/cm3 |
| 比重 |
|
ASTM D792 |
1.2 |
g/cm3 |
| 吸水率 |
24hr |
ASTM D570 |
0.02 |
% |
| 熔体流动速率 |
190℃/2.16kg |
ASTM D1238 |
8 |
g/10min |
| 热性能 丨丨 |